    OK so everyone warned me about not over heating my projects. But like the newbie I am, i over estimated what that entailed. I have over heated the roof of my '56 Studebaker Pickup. I think it's called coffee canning or soda canning? Now my roof is pretty deformed and when I try to straighten it in one spot, The other spot moved. What can I do?

  • #2
    I saw a video on you tube once about shrinking metal. Heat small areas with a torch and then cool with water. This will shrink the metal. Go easy and don't rush...
    Miller 252 Mig
    Miller Cricket XL
    Millermatic 150 Mig
    Miller Syncrowave 200 Tig
    2-O/A outfits
    Jet Lathe and Mill
    Jet 7x12 horz/vert band saw
    DeWalt Multi Cutter metal saw
    Century 50 Amp Plasma Cutter
    20 ton electric/hydraulic vertical press
    Propane Forge
    60" X 60" router/plasma table
    Vist my site:
    and check out some of my ironwork and other stuff


    • #3
      You need to shrink it back into place. The best way is with more heat than cool it quick with wet towels. There are lots of tricks to do it with a shrinking hammer and a dolly too. The best way i have seen is how the guys over at the metalworkers site do it. Is take an old SS fry pan lid and put it on a buffer and go over the area to heat it up then cool it quick with the towels. You must use a buffer for low speeds not a 20,000 rpm grinder that will make a missle. You may be able to turn an abrasive disc around backwards and run the paper side to make heat with a disc grinder you will have to try it. I will dig up some info...Bob
      Bob Wright

      Spool Gun conversion. How To Do It. Below.


      • #4
        The term is oil-canning. Yes you need to do some shrinking in the RIGHT areas, and the RIGHT way. The torch/water idea, well shrinking, also makes that spot hard, causes stress, and almost impossible to work out, so I would avoid it at all costs. Using heat, some sand bags, and a spoon you can work out oil cans pretty quickly. Visit for some learning material and tools if you dont have them. Oh and I wouldnt bother with a "shrinking disk" either, that works on the same principal as the torch/water. Been there, tried it, tossed it.
        "Better Metalworking Through Research"

        Miller Dynasty 300DX
        Miller Dynasty 200DX
        Miller Spectrum 375 extreme
        Miller Millermatic Passport

        Miller Spot Welder
        Motor-Guard stud welder

        Smith, Meco, Oxweld , Cronatron, Harris, Victor, National, Prest-o-weld, Prest-o-lite, Marquette, Century Aircraft, Craftsman, Goss, Uniweld, Purox, Linde, Eutectic, and Dillon welding torches from 1909 to Present. (58 total)


        • #5
          Thanks Guys, I thought I was completely screwed.


          • #6
            Trip over to San Jac So. to the autobody class shop, ask for David Brasden(sic) or Jake Staul, the chief instructor and his assistant, they can give ya some pointers to eliminate the oil can effect.
            Good luck